Nickel Alloy 200 201 Plate, China Nickel Alloy 200 201 Plate Manufacturers, Suppliers, Factory

Brand Name:	Guoyin
Model Number:	Nickel Alloy 200 201 Plate
Certification:	ISO;CE
Minimum Order Quantity:	3
Packaging Details:	Waterproof paper+ wooden pallet or as customers' requirement
Delivery Time:	7-15 days
Payment Terms:	T/T or L/C at sight.

Quick Detail

Nickel 200 and 201 plate offer outstanding corrosion resistance to caustic soda and other alkalis. They perform best in reducing environments but can also be used under oxidizing conditions when a passive oxide film is formed. They are used in aerospace, chemical and petrochemical processing, food processing, and marine and water treatment applications. Nickel 200 and 201 are both highly ductile across a wide temperature range and can be easily welded and processed by standard shop fabrication practices.

Specifications

Product Name	Nickel Alloy 200 201 Plate
Thickness	0.3mm-200mm
Length	2000mm, 2438mm, 3000mm, 5800mm, 6000mm, 12000mm, etc.
Width	40mm-600mm, 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc.
Standard	ASTM, AISI, JIS, GB, DIN, EN, etc.
Surface	BA, 2B, NO.1, NO.4, 4K, HL, 8K, etc.
Certificate	ISO, SGS, BV
Production Technology	Hot Rolling, Cold Rolling

Mechanical Properties

Nickel 200/201, Typical Values at 70°F (21°C), Plate—Hot Rolled, Annealed

	Yield Strength0.2% Offset		Ultimate TensileStrength		Elongationin 2 inches	Hardness
	ksi	MPa	ksi	MPa	%	Brinell(3000-kg)	RockwellB
Nickel 200	15–40	105–275	55–80	380–550	60–40	90–140	45–73
Nickel 201	12–35	83–240	50–70	345–485	60–40	—	—

Physical Performance

	Units	Temperature in°C
Density	0.321 lbs/in3	8.89 g/cm3
Specific Heat	0.109BTU/lb-°F (32—212°F)	456 J/kg-°K (0—100°C)
Modulus of Elasti city 78°F (26°C)	29.7 x 103 ksi	205 GPa (20°C)
Thermal Conductivity 212°F (100°C)	463 BTU-in/ft2-h-°F	66.5 W/m-°C
Melting Range	2615 – 2635°F	2615 – 2635°F
Electrical Resistivity	58 Ohm-circ mil/ft at 70°F	0.096 µΩ/m at 20°C

Chemical Composition

Weight % (all values are maximum unless a range is otherwise indicated)

Element	Nickel 200	Nickel 201
Nickel (plus Cobalt)	99.0 minimum	99.0 minimum
Copper	0.25	0.25
Iron	0.40	0.40
Manganese	0.35	0.35
Carbon	0.15	0.02
Silicon	0.35	0.35
Sulfur	0.01	0.01